Specifications
Brand Name :
JUNHE
Model Number :
310B
Certification :
ISO9001 TS16949
Place of Origin :
Changzhou in china
MOQ :
100 Kilograms
Price :
Negotiable
Supply Ability :
2 Tons per Day
Delivery Time :
Ten days after receipt of advance payment
Packaging Details :
Pack A:16kg/ Metal Barrel Pack B:24KG Plastic Barrel Pack C:Based on the amount of B agent A
Color :
Silver
PH :
3.8-5.2
Specific gravity :
1.30±0.05
Viscosity :
20~60s(Spray Coating) 60~90S(Dip-Spin Coating)
Cr6+ :
≥25g/L
name :
Zinc Coating
Description

Low Form Dip Spin Coating / High Dipping Speed Electroplated Zinc Coating

Dacromet anti-corrosion coating characteristics

1.1 anti-corrosion mechanism Dacromet coating, the appearance of matte silver gray, from the very fine sheet metal zinc, aluminum and chromate and other ingredients. After the workpiece in the degreasing, shot blasting treatment, dip Tu Duo Luo liquid.

Dacromet liquid is a water-based treatment solution, metal parts in the water-based treatment solution dip or spray, and then into the furnace curing, about 300 ℃ baking film, and the formation of zinc, aluminum, chromium inorganic coating Floor.

2. Coating Process

Mix Ratio

Pack A:16.0 kg

Pack B:24.0 kg (the quantity can be increased appropriately if spray coating)

Pack C:0-50 g (according to different viscosity demand )

3


Mixture Method

Before Mixture, Keep weighted A&B into the water bath at 25±2℃ , then stir A to make metal slurry disperse uniformly by frequency mixer ,after A is fully evenly dispersed, reduce the agitating speed to 60r/min, and add B.
3.2.2

Add B to the stirring A slowly. At the moment ,the barrel temperature will go up,when it reaches 35℃, startup refrigerating device to keep the barrel temperature constant at 35℃.

4. Technical data

No. Item Data
1 PH 3.8-5.2
2 Cr6+ ≥25g/L
3 Specific gravity 1.30±0.05
4 Viscosity 20~60s(Spray Coating) ; 60~90S(Dip-Spin Coating) . 20℃ Zahn 2# cup
5 Operating temperature 22±2℃

5. Coating Process

Low Form Dip Spin Coating / High Dipping Speed Electroplated Zinc Coating

6.1 Degreasing

The workpiece should be degreased if there is oil on the surface. There are three processing methods:

1.High temperature

2.Neutral water-base degreasing agent

3.Organic solvent such as methylene chloride.

6.2 Derusting

The workpiece can not be coated if there is rust or burr on the surface.The best processing method is shot blasting. The corrosion resistance of coating will be effected if acid cleaning adopted.

6.3 Coating

The workpiece afer degreasing and shot blasting should be coated through Dip-Spin coating or Spraying Coating.

6.4 Pre-heating

The workpiece after coated should be Pre-heated as soon as possible at 80~150℃ for 8~15 mins to evaporate. ( according to heat absorption of workpiece.)

6.5 Curing

The workpiece after pre-heating should be cured at 300-340℃ for 20-40 mins. ( according to heat absorption of workpiece.)

Low Form Dip Spin Coating / High Dipping Speed Electroplated Zinc Coating

Low Form Dip Spin Coating / High Dipping Speed Electroplated Zinc Coating

Product tags

spin coating system

,

spin coating theory

,

spin coating technique
Send your message to this supplier
Send Now

Low Form Dip Spin Coating / High Dipping Speed Electroplated Zinc Coating

Ask Latest Price
Watch Video
Product Detail
Brand Name :
JUNHE
Model Number :
310B
Certification :
ISO9001 TS16949
Place of Origin :
Changzhou in china
MOQ :
100 Kilograms
Price :
Negotiable
Contact Supplier
video
Low Form Dip Spin Coating / High Dipping Speed Electroplated Zinc Coating
Low Form Dip Spin Coating / High Dipping Speed Electroplated Zinc Coating
Low Form Dip Spin Coating / High Dipping Speed Electroplated Zinc Coating

Changzhou Junhe Technology Stock Co.,Ltd

Verified Supplier
9 Years
changzhou
Since 1998
Business Type :
Manufacturer
Main Products :
Zinc Flake Coating, Dacromet Coating, Dip Spin Coating Machine
Total Annual :
1300-1500
Employee Number :
200~250
Certification Level :
Verified Supplier
Discover similar products
View More