TC600 Hybrid Microwave PCB Board 15mil Thickness With Immersion Silver
TC600 Hybrid Microwave PCB Board 15mil Thickness With Immersion Silver
TC600 Hybrid Microwave PCB Board 15mil Thickness With Immersion Silver
TC600 Hybrid Microwave PCB Board 15mil Thickness With Immersion Silver
TC600 Hybrid Microwave PCB Board 15mil Thickness With Immersion Silver
TC600 Hybrid Microwave PCB Board 15mil Thickness With Immersion Silver
Specifications
Brand Name :
Bicheng
Model Number :
BIC-195.V1.0
Certification :
UL, ISO9001, IATF16949
Place of Origin :
CHINA
MOQ :
1PCS
Price :
USD9.99-99.99
Payment Terms :
T/T
Supply Ability :
5000PCS per month
Delivery Time :
8-9 working days
Packaging Details :
Vacuum bags+Cartons
Base material :
Ceramic Filled PTFE/Woven Fiberglass
Layer count :
Double Sided PCB, Multilayer PCB, Hybrid PCB
PCB thickness :
15mil (0.381mm), 20mil (0.508mm), 25mil (0.635mm), 30mil (0.762mm), 50mil (1.27mm), 60mil (1.524mm), 75mil (1.905mm), 100mil (2.54mm), 125mil (3.175mm), 150mil (3.81mm), 200mil (5.08mm), 250mil (6.35mm), 275mil (6.985mm), 500mil (12.7mm)
PCB size :
≤400mm X 500mm
Solder mask :
Green, Black, Blue, Yellow, Red etc.
Copper weight :
0.5oz (17 µm), 1oz (35µm), 2oz (70µm)
Surface finish :
Bare copper, HASL, ENIG, Immersion silver, Immersion tin, OSP, Pure gold plated etc..
Description

TC600 Microwave PCB with 15mil 20mil 30mil 50mil 60mil Thickness TC600 High Frequency PCB with Immersion Silver

(Printed Circuit Boards are custom-made products, the picture and parameters shown are just for reference)

General Description

Rogers' (Arlon) TC600 is a woven fiberglass reinforced, enhanced thermal conductivity ceramic filled, PTFE-based composite. It is designed to provide enhanced heat-transfer through“Best-In-Class” thermal conductivity, while reducing dielectric loss and insertion loss. The increased thermal conductivity (1.1 W/mk) provides higher power handling, reduces hot-spots and improves device reliability. Lower losses result in higher amplifier and antenna gains/efficiencies. Stable dielectric constant is across a wide temperature range (-75 ppm/oC -40°C to 140°C). It helps power amplifier and antenna designers maximize gain and minimize dead bandwidth lost to dielectric constant drift as operating temperature changes. It has low Z-Direction CTE and mechanical robustness is also greatly improved for the 6.15 dielectric constant market.

Features

1. Very Low Loss Tangent (0.002 at 10 GHz) provides Higher Amplifier or Antenna Efficiency

2. Mechanically Robustness improves processing and reliability, replaces brittle laminates that cannot withstand processing, impact or High Gain forces

3. Low coefficient of thermal expansion on X,Y and Z axis (9, 9 and 35 ppm/°C) matches active components for low stress solder joints

4. High Peel Strength for Reliable narrow lines

Benefits

1. Reduced Heat Generated through Transmission Line Loss

2. Heat Dissipation and Management

3. Replace Ceramic in Some Applications

4. Large Panel Sizes for Multiple Circuit Layout for lowered Processing Costs

Typical Properties TC600

1. Electrical Properties
Dielectric Constant (may vary by thickness)
@1.8 MHz - 6.15 Resonant Cavity
@10 GHz - 6.15 IPC TM-650 2.5.5.5
Dissipation Factor
@1.8 GHz - 0.0017 Resonant Cavity
@10 GHz - 0.002 IPC TM-650 2.5.5.5
Temperature Coefficient of Dielectric -
TCεr @ 10 GHz (-40-150°C) ppm/ºC -75 IPC TM-650 2.5.5.5
Volume Resistivity
C96/35/90 MΩ-cm 1.6x109 IPC TM-650 2.5.17.1
E24/125 MΩ-cm 2.4x108 IPC TM-650 2.5.17.1
Surface Resistivity
C96/35/90 MΩ 3.1x109 IPC TM-650 2.5.17.1
E24/125 MΩ 9.0x108 IPC TM-650 2.5.17.1
Electrical Strength Volts/mil (kV/mm) 850 (34) IPC TM-650 2.5.6.2
Dielectric Breakdown kV 62 IPC TM-650 2.5.6
Arc Resistance sec >240 IPC TM-650 2.5.1
2. Thermal Properties
Decomposition Temperature (Td)
Initial °C 512 IPC TM-650 2.4.24.6
5% °C 572 IPC TM-650 2.4.24.6
T260 min >60 IPC TM-650 2.4.24.1
T288 min >60 IPC TM-650 2.4.24.1
T300 min >60 IPC TM-650 2.4.24.1
Thermal Expansion, CTE (x,y) 50-150ºC ppm/ºC 9, 9 IPC TM-650 2.4.41
Thermal Expansion, CTE (z) 50-150ºC ppm/ºC 35 IPC TM-650 2.4.24
% z-axis Expansion (50-260ºC) % 1.5 IPC TM-650 2.4.24
3. Mechanical Properties
Peel Strength to Copper (1 oz/35 micron)
After Thermal Stress lb/in (N/mm) 10 (1.8) IPC TM-650 2.4.8
At Elevated Temperatures (150ºC) lb/in (N/mm) 10 (1.8) IPC TM-650 2.4.8.2
After Process Solutions lb/in (N/mm) 9 (1.6) IPC TM-650 2.4.8
Young’s Modulus kpsi (MPa) 280 (1930) IPC TM-650 2.4.18.3
Flexural Strength (Machine/Cross) kpsi (MPa) 9.60/9.30 (66/64) IPC TM-650 2.4.4
Tensile Strength (Machine/Cross) kpsi (MPa) 5.0/4.30 (34/30) IPC TM-650 2.4.18.3
Compressive Modulus kpsi (MPa) ASTM D-3410
Poisson’s Ratio - ASTM D-3039
4. Physical Properties
Water Absorption % 0.02 IPC TM-650 2.6.2.1
Density, ambient 23ºC g/cm3 2.9 ASTM D792 Method A
Thermal Conductivity (z-axis) W/mK 1.1 ASTM E1461
Thermal Conductivity (x, y) W/mK 1.4 ASTM E1461
Specific Heat J/gK 0.94 ASTM E1461
Flammability class V0 UL-94
NASA Outgassing, 125ºC, ≤10-6 torr
Total Mass Loss % 0.02 NASA SP-R-0022A
Collected Volatiles % 0 NASA SP-R-0022A
Water Vapor Recovered % 0 NASA SP-R-0022A

TC600 Hybrid Microwave PCB Board 15mil Thickness With Immersion Silver

Our PCB Capability (TC600)

PCB Material: Ceramic Filled PTFE/Woven Fiberglass
Designation: TC600
Dielectric constant: 6.15 (10 GHz)
Dissipation Factor 0.002 (10 GHz)
Layer count: Double Sided PCB, Multilayer PCB, Hybrid PCB
Copper weight: 0.5oz (17 µm), 1oz (35µm), 2oz (70µm)
Dielectric thickness: 15mil (0.381mm), 20mil (0.508mm), 25mil (0.635mm), 30mil (0.762mm), 50mil (1.27mm), 60mil (1.524mm), 75mil (1.905mm), 100mil (2.54mm), 125mil (3.175mm), 150mil (3.81mm), 200mil (5.08mm), 250mil (6.35mm), 275mil (6.985mm), 500mil (12.7mm)
PCB size: ≤400mm X 500mm
Solder mask: Green, Black, Blue, Yellow, Red etc.
Surface finish: Bare copper, HASL, ENIG, Immersion silver, Immersion tin, OSP, Pure gold plated etc..

Typical Applications:

1. Digital Audio Broadcasting (DAB) Antennas (Satellite Radio)

2. GPS & Hand-held RFID Reader Antennas

3. Microwave Combiner and Power Divider Boards in Avionics Applications

4. Power Amplifiers, Filters and Couplers

5. Small Footprint Antennas

TC600 Hybrid Microwave PCB Board 15mil Thickness With Immersion Silver

Send your message to this supplier
Send Now

TC600 Hybrid Microwave PCB Board 15mil Thickness With Immersion Silver

Ask Latest Price
Product Detail
Brand Name :
Bicheng
Model Number :
BIC-195.V1.0
Certification :
UL, ISO9001, IATF16949
Place of Origin :
CHINA
MOQ :
1PCS
Price :
USD9.99-99.99
Contact Supplier
TC600 Hybrid Microwave PCB Board 15mil Thickness With Immersion Silver
TC600 Hybrid Microwave PCB Board 15mil Thickness With Immersion Silver
TC600 Hybrid Microwave PCB Board 15mil Thickness With Immersion Silver

Bicheng Electronics Technology Co., Ltd

Verified Supplier
6 Years
guangdong, shenzhen
Since 2003
Business Type :
Manufacturer, Distributor/Wholesaler, Exporter, Seller
Main Products :
RF PCB Board, Rogers PCB Board, Taconic PCB
Total Annual :
10 million-18 million
Employee Number :
350~450
Certification Level :
Verified Supplier
Discover similar products
View More

Find Similar Products By Category:

Supplier Homepage Products High Speed PCB
MachineU China Products Home Appliance Home Appliance Parts Kitchen Appliance Parts Microwave Oven Parts
Contact Supplier
Submit Requirement