Ultra Thin Ultra Clear Aluminosilicate Glass For Anti-reflective Display Cover Glass

Alumino-Silicate Glass (Purple Horn-M2) is an eco-friendly high aluminosilicate ultra-thin glass, which increases the Al₂O₃ content in the composition to improve the ion exchange efficiency, so that it has excellent mechanical properties after chemical strengthening.

Features:

• High Impact Resistance

• High Scratch Resistance

• High Transmittance

• High chemical resistance

• High Flexibility

• High Bending Strength Resistance

• Ultra Clear White

Purple Horn-M2’s 0.25~2.5mm thickness high alumino-silicate glass has already been used in the market to meet a wide range of customers needs.

Application: Widely used in High-end Consumer Electronics Device Cover such as cellphone, tablet, laptop, computer display, Vehicle Display, Industrial Touch Panels, Smart Home Screen Display etc fields;

Regular Thickness: 0.25mm~2mm

Standard Size:1300*1100mm (5th Generation)

Note: The size can be customized according to customer's needs.

Product Composition

Alumino-Silicate Glass achieves better stress and strain depth than ordinary soda-lime glass by increasing the Al₂O₃ content in the glass and increasing the ion exchange capacity.

Physical Property Parameter

Chemical Tempering Process Parameter

Note: Tempering solution Na+<0.5%. The above test results are affected by processing conditions, the data is for reference only, not as a basis for production.

Packaging Diagram

Storage Conditions: Temperature ≤30℃, humidity ≤65% (no condensation), shelf life is 6 months from the date of delivery.

High Alumino-Silicate Glass(Purple Horn-H1) is adopted Float Glass Process.

Float glass is made by heating raw materials—silica sand, limestone, soda ash, and magnesium in a furnace. When melted, it’s then spread out over a sizable bed of molten tin. As it moves along rollers in the annealing oven during a controlled cooling process, this mixture slowly solidifies over the molten tin. From this point, a single, continuous smooth ribbon of glass emerges as below picture showed: