NO.  | Physical Property  | ISO  | Unit  | Result  | ||||
1.  | Specific gravity / density  | D792  | Kg/m  | 1175  | ||||
Optical  | ||||||||
2.  | Luminous Transmittance  | GB/T2410-2008  | %  | 92.6  | ||||
3.  | Haze  | GB/T2410-2008  | %  | 1.8  | ||||
Mechanical  | ||||||||
4.  | Tensile Strength  | 527-2:2012  | ||||||
a) Maximum tensile strength  | MPa  | 80.7  | ||||||
b) Elongation at break  | %  | 4  | ||||||
c)Tensile modulus  | MPa  | 3010  | ||||||
5.  | Flexural Strength  | 178:2010  | ||||||
a) Maximum flexural strength  | MPa  | 87.7  | ||||||
b) Maximum flexural strength  | MPa  | 2900  | ||||||
6.  | Comintsane Yield Stress  | 604:2002  | MPa  | No Yield Point  | ||||
7.  | Izod Notched Immpact Stress  | D256-10 (Method c)  | J/m  | 8  | ||||
8.  | Shear Strength  | D732-10  | MPa  | 62.5  | ||||
9.  | Rockwell Hardness  | 2039-2:1987  | HRL  | 105  | ||||
Thermal  | ||||||||
10.  | Flammability  | UL94-2013 (7)  | mm/min  | 24.1  | ||||
11.  | Heat Deflection Temperature  | 75-2:2013(Method B)  | °C  | 106.2  | ||||
12.  | Glass Transition Temperature  | 11357-2:1999  | ||||||
a)Teig  | °C  | 105.6  | ||||||
b)Tmg  | °C  | 114.0  | ||||||
c)Tefg  | °C  | 122.3  | ||||||
13.  | Coefficient of Linear Thermal Expansion  | 11359-2:1999  | °C  | -40 to 110  | ||||
a)Parallel to flow  | um/m-°C  | 78.60  | ||||||
b)Perpendicular to flow  | um/m-°C  | 80.56  | ||||||
Others  | ||||||||
14.  | Water Absorption  | 62:2008  | %  | 0.12  | ||||
15.  | Odor  | None  | ||||||
16.  | Taste  | None  | ||||||